湘西地区微细粒级难选菱锰矿浮选试验研究

湘西地区菱锰矿呈细粒或微细粒状态嵌布,且脉石繁多结构复杂,属于难选菱锰矿。采用X射线荧光光谱、X射线衍射及MLA等方法对菱锰矿进行了全面的工艺矿物学研究。针对微细粒级难选菱锰矿,以合适的Mn品位和回收率为指标,考察了磨矿细度、pH调整剂用量、抑制剂用量以及捕收剂用量对菱锰矿浮选的影响。试验表明,菱锰矿(Mn品位9.93%)在磨矿细度-0.074 mm 95.66 %的条件下,采用"一粗一精一扫"的正浮选试验流程,可获得精矿Mn品位19.04 %、Mn回收率88.86 %的浮选指标。     

55SiCr弹簧钢中的残留奥氏体与碳化物

通过扫描电镜(SEM)、电子背散射衍射(EBSD)、透射电镜(TEM)、X射线衍射仪(XRD)、热膨胀仪、洛氏硬度计等手段研究了弹簧钢55SiCr的组织和相变点以及残留奥氏体和碳化物在热处理过程中的组织演变。结果表明:55SiCr弹簧钢淬火后残留奥氏体以块状分布在基体上;随回火温度的升高,残留奥氏体减少并呈粒状和薄膜状分布;C在残留奥氏体中富集,使其稳定性增强;Si抑制了碳化物的析出,提高了残留奥氏体的稳定性。低温回火时,Si延缓了渗碳体析出;高温回火时,C原子扩散速率提高,促进渗碳体析出,引起体积的收缩。慢速加热回火时,C有足够的时间扩散,从而促进渗碳体的形成,使渗碳体的形成温度提前;快速加热回火时,C来不及扩散,抑制了渗碳体的析出。回火加热速率一样时,试验钢的硬度随回火温度的提高而下降。当回火温度为400 ℃时,硬度值最大为51 HRC;当回火温度为650 ℃时,硬度值最小为37 HRC。当加热速率为0.1 ℃/s时,硬度值最小为33 HRC;当加热速率为200 ℃/s时,硬度值最大为40 HRC。     

浅谈水泥窑大修外包的安全管理问题

水泥窑大修由外协单位承接比较普遍。这种方式,存在安全责任归属不明确、以合同代替管理、以罚款代替管理的现象,缺少完善的对外协单位安全绩效评价体系。而外协单位私营性质居多,缺乏规范有效的安全管理体系,人员流动性比较大,一人持证多人跟班。我公司将水泥窑大修外协单位纳入公司安全管理体系,建立了入场前告知制度;具体项目建立"安全管理微信工作群",统一协调检修安全工作;作业开始前组织对外协单位人员进行全员安全交底;及时组织对危险作业点和安全风险较大的交叉作业点进行风险评估;全天候安排专业人员监督检查;强化安全违章诫勉谈话机制;监督各相关方做好检修安全自检自查工作;及时组织对相关方进行安全绩效评价。     

2K-H型人字齿周转轮系的免组装设计与成型

为了解决人字齿周转轮系加工、装配的难题,提出利用3D打印技术制造免组装人字齿周转轮系的新工艺。通过理论推导,建立变位系数、齿侧间隙与齿轮基本参数之间的关系。利用建立的关系式,对行星轮进行负变位,设计具有微量齿侧间隙的2K-H型人字齿周转轮系。利用熔融沉积成型实验平台使设计的人字齿周转轮系成型,成型后的人字齿周转轮系齿轮啮合传动正常,设计、制作相应辅件,将其装配成减速步进电机。结果表明,通过合适的间隙设计,可以利用3D打印技术实现人字齿周转轮系的免组装制造,为小尺寸、一体式人字齿周转轮系个性化定制提供了一种具有工业应用前景的全新解决方案。     

深埋矿体移动带三维圈定方法及应用

针对深埋矿山开采移动带二维圈定方法工作量大、精度低且难以满足日益增长的经济效益需求的问题，提出了一种深埋复杂矿体移动范围三维确定方法。结合沙岭金矿千米深井工程实例，在移动范围确定过程中，借助先进的3D建模技术获得三维矿山模型。该模型可以实现各类地质体的可视化，直观地展示其形态与产状，清晰地反映各构成因素间的相互关系。在3D模型中截取的特征剖面与经典移动带圈定岩移参数获取方法相结合，能轻松获得各特征剖面上的岩移参数值。通过给定的岩移参数值进而确定各特征剖面上的地表移动边界点，将各移动边界点连接即可实现矿山移动范围的圈定。研究结果表明，基于三维地质建模技术的移动带圈定方法合理可行，确定的纱岭金矿地表移动带能够兼顾安全生产与经济效益，为矿山生产开发奠定了有益基础，为类似矿山提供了有益借鉴。     

Polytetrafluoroethylene-intercalated MXene membranes with good photothermal performance for enhanced laser ignition

Photothermal effect has been widely used in many areas such as cancer therapy, photothermal energy harvesting, and laser ignition. However, exploring reliable and efficient free-standing energy converter for enhancing the photothermal performance is still a challenge. Herein, free-standing membrane based on two-dimensional MXene (Ti₃C₂) nanosheets and polytetrafluoroethylene (PTFE) was fabricated and characterized by X-ray diffraction, scanning electron microscopy and differential scanning calorimetry, which demonstrated a drastic temperature rise by laser irradiation and was further used as energy converter for enhancing the photothermal performance of laser ignition. Furthermore, the initiating power of the laser initiator can be largely reduced by adding a thin layer of MXene/PTFE membrane above the B/KNO₃ cylinder. This work can give great promise for MXene-based membranes as the laser energy converter for reducing the initiating energy and promote the development of laser initiators with low initiating energy.     

异丙醇铝控制水解制备高纯拟薄水铝石和多孔氧化铝

主要进行异丙醇铝水解制备高纯拟薄水铝石和高纯多孔γ-Al_2O_3的研究。合成路线以异丙醇铝为原料,改变反应过程中水化液组成、水化温度和水化时间,制备一系列拟薄水铝石及其焙烧产物多孔γ-Al_2O_3。结果表明,水化液中异丙醇的存在会抑制无定型氢氧化铝的晶化,但也有助于形成大孔径、高比表面和大孔容的氧化铝;纯水体系下,60℃以下水化会出现三水铝石,60℃以上水化的产物则为拟薄水铝石;γ-Al_2O_3孔结构与前驱体拟薄水铝石的结晶度有关,晶粒越大的拟薄水铝石,焙烧所得氧化铝的孔径和孔容也增大。因此,水化条件的改变可以实现拟薄水铝石结构的控制,进而获得不同结构的多孔氧化铝。为由异丙醇铝水解制备高纯拟薄水铝石和多孔氧化铝的工业化提供相应的研究基础。     

矿粉颗粒表面微观形貌对过滤性能的影响

为研究矿粉表面微观形貌对过滤性能的影响,将-200目80%的5种不同的铁精矿粉A、B、C、D、E在过滤压力0.06 MPa、过滤时间3 min的条件下进行过滤试验;并测定5种铁精粉的最大分子水和最大毛细水,用扫描电镜观察其微观形貌。试验结果表明:5种矿粉的滤饼水分、最大分子水和最大毛细水由大到小依次均是A、B、C、D、E,并且与矿粉的表面微观形貌密切相关。矿粉颗粒表面粗糙,吸附较多细小颗粒,其比表面积和表面能较大,毛细管作用较强,所含的最大分子水和最大毛细水较大;毛细管作用强使得过滤速率降低,毛细水的脱除难度增大,最终导致滤饼水分较高。     

Ni,Cr, and Fe surfaces corroded by molten ZnCl2

Understanding the corrosion of molten ZnCl₂ on metal surfaces is significant for the corrosion protection of metals, sustainable use of molten salts, preparation of ZnO coatings, and so on. In this paper, surfaces of pure Ni, Cr, and Fe corroded by molten ZnCl₂ were investigated. The results show that Ni suffered very slight corrosion, while Cr experienced more serious corrosion than Ni, but lighter corrosion than Fe. The morphology of the corrosion of Cr and Fe, respectively, presented pitting and intergranular corrosion characteristics. Furthermore, nanostructured ZnO coatings were obtained on the surfaces of Ni and Fe, but not on the surface of Cr. The ZnO coating on the Ni surface was doped with a small amount of Zn₅(OH)₈Cl₂, and the ZnO coating on the Fe surface was doped with ZnFe₂O₄ and Zn₂OCl₂. The coatings on the Ni and Fe surfaces had an average thickness of 1.5 and 50 μm, respectively.